铁合金抛光用棕色金刚砂磨料600#
铁合金抛光用棕色金刚砂磨料600#的主要成分是氧化铝，它是以铝矾土为原料，无烟煤，铁霄，在电弧中经2000度以上高温熔炼制成。然后经过磨机粉碎整形，磁选去铁，筛分成多种粒度，其质地致密、硬度高，韧性好。棕刚玉微粉的粒度分级是水洗溢流、自然沉淀烘干，纯净度更高，粒度范围窄无大颗粒，适合研磨抛光。
铁合金抛光用棕色金刚砂磨料600#产品特点
1. 棕刚玉韧性比白刚玉高，适合研磨金属件。
2. 棕刚玉微粉经过磁选和水洗，杂质少，无金属残留，研磨后不会产生锈斑。
3. 经过水力分级，粒度均匀，粒径范围窄。
4. 成本比其他研磨微粉低。
Brown fused aluminum oxide 600 grit is made of high-quality bauxite, anthracite and iron filings. It is cooled and smelted in a high temperature by more than 2000 degrees in an electric arc. It is crushed and shaped by a jaw crusher and a ball mill. After magnetic separation, then sieve separated to get various kinds. Its compact texture, high hardness, suitable for the manufacture of ceramics, grinding of high tensile metal and grinding, polishing, sandblasting media, precision casting, etc., can also be used to produce advanced refractory materials.
Application:
Brown aluminum oxide 600 grit is widely used as a raw material in many industries：
1. Laminates, coatings, lapping, polishing
2. Polishing
3. Buffing and compounds for ferrous and non-ferrous metal, ceramic, and stone.
4. Wear resistance applications
铁合金抛光用棕色金刚砂磨料600#典型化学指标
|
AL2O3 |
94.00% |
|
Fe2O3 |
0.38% |
|
Si2O |
1.45% |
|
Ti2O |
3.10% |
|
LOI |
0.08% |
|
磁性物 |
/ |
铁合金抛光用棕色金刚砂磨料600#物理指标：
|
主要矿物 |
Al2O3 |
|
硬度 |
莫氏 9.0 |
|
熔点 |
2200 ℃ |
|
使用温度 |
1850℃ |
|
比重 |
3.95g/cm3 |
|
堆积密度(LPD): |
1.53-1.99 g/cm3 |
|
颜色 |
棕色 |
|
晶形 |
三方晶系 |
棕刚玉微粉粒度：
W标
|
粒 度 |
最粗粒 |
粗粒 |
基本粒 |
混合粒 |
细粒 |
|||||
|
尺寸 范围 |
允许颗粒 |
尺寸 范围 |
重量% 不多于 |
尺寸 范围 |
重量% 不少于 |
尺寸 范围 |
重量% 不少于 |
尺寸 范围 |
重量% 不多于 |
|
|
W63 |
100-80 |
1 |
80-63 |
15 |
63-50 |
50 |
63-40 |
80 |
细于40 |
5 |
|
W50 |
80-63 |
1 |
63-50 |
15 |
50-40 |
50 |
50-28 |
80 |
细于28 |
5 |
|
W40 |
63-50 |
1 |
50-40 |
15 |
40-28 |
50 |
40-20 |
80 |
细于20 |
5 |
|
W28 |
50-40 |
1 |
40-28 |
18 |
28-20 |
45 |
28-14 |
74 |
细于14 |
8 |
|
W20 |
40-28 |
1 |
28-20 |
18 |
20-14 |
45 |
20-10 |
74 |
细于10 |
8 |
|
W14 |
28-20 |
2 |
20-14 |
20 |
14-10 |
45 |
14-7 |
72 |
细于7 |
8 |
|
W10 |
20-14 |
2 |
14-10 |
20 |
10-7 |
40 |
10-5 |
70 |
细于5 |
10 |
|
W7 |
14-10 |
2 |
10-7 |
20 |
7-5 |
40 |
7-3.5 |
70 |
细于3.5 |
10 |
2.JIS 日标
|
粒度
|
D0（um）
|
D3(um)
|
D50(um)
|
D94(um)
|
|
#240
|
127以下
|
103以下
|
57.0±3.0
|
40以上
|
|
#280
|
112以下
|
87以下
|
48.0±3.0
|
33以上
|
|
#320
|
98以下
|
74以下
|
40.0±2.5
|
27以上
|
|
#360
|
86以下
|
66以下
|
35.0±2.0
|
23以上
|
|
#400
|
75以下
|
58以下
|
30.0±2.0
|
20以上
|
|
#500
|
63以下
|
50以下
|
25.0±2.0
|
16以上
|
|
#600
|
53以下
|
41以下
|
20.0±1.5
|
13以上
|
|
#700
|
45以下
|
37以下
|
17.0±1.5
|
11以上
|
|
#800
|
38以下
|
31以下
|
14.0±1.0
|
9.0以上
|
|
#1000
|
32以下
|
27以下
|
11.5.±1.0
|
7.0以上
|
|
#1200
|
27以下
|
23以下
|
9.5±0.8
|
5.5以上
|
|
#1500
|
23以下
|
20以下
|
8.0±0.6
|
4.5以上
|
|
#2000
|
19以下
|
17以下
|
6.7±0.6
|
4.0以上
|
3.FEPA 欧标
|
粒度 |
D3(um) |
D50(um) |
D94（um) |
|
F230 |
＜82 |
53.0±3.0 |
>34 |
|
F240 |
＜70 |
44.5±2.0 |
>28 |
|
F280 |
＜59 |
36.5±1.5 |
>22 |
|
F320 |
＜49 |
29.2±1.5 |
>16.5 |
|
F360 |
＜40 |
22.8±1.5 |
>12 |
|
F400 |
＜32 |
17.3±1.0 |
>8 |
|
F500 |
＜25 |
12.8±1.0 |
>5 |
|
F600 |
＜19 |
9.3±1.0 |
>3 |
|
F800 |
＜14 |
6.5±1.0 |
>2 |
4. P标微粉粒度组成
|
粒度 |
D0（um） |
D3(um) |
D50(um) |
D95(um) |
|
P240 |
110以下 |
81.7以下 |
58.5±2.0 |
44.5以上 |
|
P280 |
101以下 |
74.0以下 |
52.2±2.0 |
39.2以上 |
|
P320 |
94以下 |
66.8以下 |
46.2±1.5 |
34.2以上 |
|
P360 |
87以下 |
60.3以下 |
40.5±1.5 |
29.6以上 |
|
P400 |
81以下 |
53.9以下 |
35.0±1.5 |
25.2以上 |
|
P500 |
77以下 |
48.3以下 |
30.2±1.5 |
21.5以上 |
|
P600 |
72以下 |
43.0以下 |
25.8±1.0 |
18.0以上 |
|
P800 |
67以下 |
38.1以下 |
21.8±1.0 |
15.1以上 |
棕刚玉金刚砂500#低硅高铝氧化铝粉产品用途
1. 磨刀石，研磨石，油石等制品的生产
2. 抛光蜡，抛光液等的生产
3. 工业研磨，抛光
4. 电子行业如电路板等电子元件、3C行业如金属手机壳打磨和研磨介质
5. 陶瓷制品，研磨抛光等
6. 地面、墙面压层材料中作为耐磨介质
7. 陶瓷釉料，地坪涂料等
8. 不锈钢仪器、五金器件研磨抛光
9. 涂附磨具